Hexagon nuts with clamping part fine thread ISO 10513-10 zinc plated blue M12x1,25

The wrench sizes for hexagon bolts and nuts are specified in ISO 272: 1982-01. The nominal wrench size on the workpiece (e.g. bolt, nut) is the same as that on the tool. However, there is some play between the two to allow the tool to be fitted without difficulty. The relationship between the nominal diameter d of the thread and the wrench size s is standardised in EN ISO 4014 and EN ISO 4017 for hexagon bolts, and in EN ISO 4032 for hexagon nuts (dimensions in mm).

For nuts, only a single digit is used, which indicates the maximum strength class of the bolt with which the nut can be used (a strength class 10 nut can be used with an 8.8 or 10.9 bolt, but not with a 12.9 bolt).

Steel is an iron-carbon alloy with a maximum carbon content of 2% by mass. The steels achieve their intended physical and mechanical properties through various hardening, annealing and tempering processes. It is also possible to harden the edge zone by surface hardening, case hardening or nitriding. Well-known steel grades are structural steels, free-machining steels, case-hardening steels, nitriding steels, tempering steels, tool steels and stainless steels.

Blue galvanised finishes are produced either by electroplating in accordance with DIN EN ISO 4042 or by mechanical plating in accordance with DIN EN ISO 12683. For fasteners with a hardness exceeding 390 HV, there is a risk of hydrogen embrittlement during galvanising (electrolytic process). This necessitates specific measures (such as annealing), although these do not provide a 100 per cent guarantee against embrittlement.

Stainless steels are defined in DIN EN 10088-1 as iron alloys containing at least 10.5 per cent chromium and no more than 1.2 per cent carbon. The multi-part DIN EN ISO 3506 series of standards applies to mechanical fasteners made from stainless steels. Grade A4 is classified as acid-resistant due to its molybdenum content of 2 per cent to 3 per cent. A4 cannot be heat-treated and achieves its various strength classes through cold working to different degrees.