Hexagon nuts with clamping part fine thread ISO 10513-8 zinc plated blue M8x1

The wrench sizes for hexagon bolts and nuts are specified in ISO 272: 1982-01. The nominal wrench size on the workpiece (e.g. bolt, nut) is the same as that on the tool. However, there is some play between the two to allow the tool to be fitted without difficulty. The relationship between the nominal diameter d of the thread and the wrench size s is standardised in EN ISO 4014 and EN ISO 4017 for hexagon bolts, and in EN ISO 4032 for hexagon nuts (dimensions in mm).

Only one number is used for nuts. This indicates up to which strength class of the screw the nut can be used. For example, you can use a nut strength class 8 with a screw 8.8, but not with a screw 10.9. If you use nuts with a strength class that is too low, there is a risk of the thread stripping. Higher ones can be used without hesitation, but should only be used if the load on the screw is above the yield point.

Steel is an iron-carbon alloy with a maximum carbon content of 2% by mass. The steels achieve their intended physical and mechanical properties through various hardening, annealing and tempering processes. It is also possible to harden the edge zone by surface hardening, case hardening or nitriding. Well-known steel grades are structural steels, free-machining steels, case-hardening steels, nitriding steels, tempering steels, tool steels and stainless steels.

Blue galvanised finishes are produced either by electroplating in accordance with DIN EN ISO 4042 or by mechanical plating in accordance with DIN EN ISO 12683. For fasteners with a hardness exceeding 390 HV, there is a risk of hydrogen embrittlement during galvanising (electrolytic process). This necessitates specific measures (such as annealing), although these do not provide a 100 per cent guarantee against embrittlement.

Stainless steels are defined in DIN EN 10088-1 as iron alloys containing at least 10.5 per cent chromium and no more than 1.2 per cent carbon. The multi-part DIN EN ISO 3506 series of standards applies to mechanical fasteners made from stainless steels. Grade A4 is classified as acid-resistant due to its molybdenum content of 2 per cent to 3 per cent. A4 cannot be heat-treated and achieves its various strength classes through cold working to different degrees.