Slotted set screws and spigot DIN 417-stainless A2 M8x12 mm

Stainless steel refers to alloyed or unalloyed steels that contain at least 10.5% chromium and less than 1.2% carbon. Colloquially, stainless steel is also referred to as stainless steel (NiRo), although not all stainless steel is the same as "stainless".

The term plain indicates a completely untreated, merely oiled, smooth surface for all DIN and ISO screws such as wood screws, hexagon head screws, threaded rods, nuts and many types of washers.

Slotted screw drives are the oldest form of rotary drives for fastening screws. The Schltz is usually manufactured in a pressed or milled version. Because of its uneconomical processing method (slow, unwieldy), the slot is increasingly disappearing in favor of other drives (hexagon socket, cross slot, hexagon socket).

Grade 1.4305 is a sulphurised austenitic stainless steel of the A1 type. It is specifically intended for machining. Due to its high sulphur content of up to 0.35 per cent, this material has lower corrosion resistance than comparable stainless steels with a typical sulphur content of no more than 0.015 per cent. It is not suitable for use in non-oxidising acids and media or in chloride-containing environments (such as marine environments, etc.).

Stainless steels are defined in DIN EN 10088-1 as iron alloys containing at least 10.5 per cent chromium and no more than 1.2 per cent carbon. The multi-part DIN EN ISO 3506 series of standards applies to mechanical fasteners made from stainless steels. Grade A2 is classified as non-acid-resistant. Austenitic stainless steels cannot be heat-treated and achieve their different strength classes through cold working to varying degrees.