Sechskantschrauben mit Schaft DIN 931-10.9 gsw M8x35

Steel is an iron-carbon alloy with a maximum carbon content of 2% by mass. The steels achieve their intended physical and mechanical properties through various hardening, annealing and tempering processes. It is also possible to harden the edge zone by surface hardening, case hardening or nitriding. Well-known steel grades are structural steels, free-machining steels, case-hardening steels, nitriding steels, tempering steels, tool steels and stainless steels.

The tempering process of screws and nuts (heating - holding - quenching - tempering) results in a thin baked oxide layer, which is referred to as tempered black. This surface condition is not a surface coating and therefore offers no corrosion protection.

The wrench sizes for hexagon bolts and nuts are specified in ISO 272: 1982-01. The nominal wrench size on the workpiece (e.g. bolt, nut) is the same as that on the tool. However, there is some play between the two to allow the tool to be fitted without difficulty. The relationship between the nominal diameter d of the thread and the wrench size s is standardised in EN ISO 4014 and EN ISO 4017 for hexagon bolts, and in EN ISO 4032 for hexagon nuts (dimensions in mm).

The number before the point multiplied by one hundred gives the nominal value of the tensile strength in N/mm2, the number before the point multiplied by the number after the point and multiplied by 10 gives the nominal value of the 0.2% yield strength in N/mm2. The number after the decimal point provides information about the yield strength, as a percentage of the tensile strength.