Hex Head screws fully threaded DIN 933-8.8 zinc plated blue PA spot coated M10x25 mm

The polyamide spot coating creates a clamping effect when the screw is tightened. The storage life is 4 years. The coating is applied in accordance with DIN 267-28 and acts purely as a loss prevention measure under dynamic loads. It does not prevent the screw from loosening or coming undone.

Steel is an iron-carbon alloy with a maximum carbon content of 2% by mass. The steels achieve their intended physical and mechanical properties through various hardening, annealing and tempering processes. It is also possible to harden the edge zone by surface hardening, case hardening or nitriding. Well-known steel grades are structural steels, free-machining steels, case-hardening steels, nitriding steels, tempering steels, tool steels and stainless steels.

Blue galvanised finishes are produced either by electroplating in accordance with DIN EN ISO 4042 or by mechanical plating in accordance with DIN EN ISO 12683. For fasteners with a hardness exceeding 390 HV, there is a risk of hydrogen embrittlement during galvanising (electrolytic process). This necessitates specific measures (such as annealing), although these do not provide a 100 per cent guarantee against embrittlement.

The wrench sizes for hexagon bolts and nuts are specified in ISO 272: 1982-01. The nominal wrench size on the workpiece (e.g. bolt, nut) is the same as that on the tool. However, there is some play between the two to allow the tool to be fitted without difficulty. The relationship between the nominal diameter d of the thread and the wrench size s is standardised in EN ISO 4014 and EN ISO 4017 for hexagon bolts, and in EN ISO 4032 for hexagon nuts (dimensions in mm).

The number before the point multiplied by one hundred gives the nominal value of the tensile strength in N/mm2, the number before the point multiplied by the number after the point and multiplied by 10 gives the nominal value of the 0.2% yield strength in N/mm2. The number after the decimal point provides information about the yield strength, as a percentage of the tensile strength.